TRINIAETH GWRES DUR STEEL HEAT TREATMENT

1
TRINIAETH GWRESDURSTEELHEAT TREATMENT
2
Pwrpas trin metelau trwy eu cynhesu au oeri ydi
newid eu priodweddion er mwyn eu gwneud yn fwy
defnyddiol Mae 4 prif triniaeth Caledu Gwydno Norm
aleiddio Analeiddio
The purpose of treating metals by heating and
cooling is to change their properties to make
them more useful There are 4 main
treatments Harden Toughen Normalise Annealing
3
Mae trin metalau yn gywir yn dibynnu ar tri
pheth 1 Gwres pa dymheredd fydd angen ei
gyrraedd 2 Carbon Faint o carbon sydd yn y
dur 3 Oeri sut mae oeri y metel yn effeithio
ar y priodweddion Ar y dudalen nesaf welwch
DEIAGRAM HAEARN CARBON. Mae hwn yn BWYSIG iawn
o hwn me peiriannwyr yn penderfynnu dut i drin
metel. Maen disgrifio metel ar lefel
adeiladwaith moleciwlaidd Ferrite meddal a
hydwyth, Pearlite Gwydn, Cementite caled ond
brau. Mae adeiladwith dur yn newid pan yn ei
gynhesu ac maer diagram yn dangos fod dur gyda
0.85 carbon ar dymheredd o 700 oC wedi cyrraedd
y pwynt Eutectoid sef defnydd Caled ond gwydn
perfaith.
Correct heat treatment depends on three things 1-
Heat what temperature do we need to heat the
steel 2. Carbon whats the steels carbon
content 3. Cooling how its cooled effects the
properties On the next page is the IRON CARBON
DIAGRAM. This is very important and forms the
basis of all steel heat treatment. It shows what
happens to steels structure when heated at a
molecular level Ferrite soft and ductile,
Pearlite is tough, Cementite hard and
brittle. The structure of steel changes when
heated and the diagram shows that steel with
0.85 carbon heated to 700oC will reach the
Eutectoid Point a strong and tough balanced
steel.
4
(No Transcript)
5
CALEDU Pwrpas caledu ydi gwneud dur yn galetach
proses syml o gynhesu ac wedyn oeri yn sydyn.
Maer diagram ar y dudalen nesaf yn dangos y
tymheredd sydd angen ei gyrraedd cyn oeri y dur
maen dangos ni allwch caledu dur gyda llai na
0.3 Carbon. Oeri Maer tabl isod yn dangos
beth mae oeri dur mewn hylif gwahanol yn ei wneud
I briodweddion y dur eto yn ddibynnol ar
cynnwys carbon y dur
HARDENING Its purpose is to make steel harder
a simple process heat the steel then cool
quickly. The Diagram on the next page shows
hardening temperatures for different carbon
values it also shows you cannot harden steel
less than 0.3 Carbon. Cooling table below
shows how cooling or quenchinh in different
liquids affect the properties depending on the
carbon present.
6
(No Transcript)
7
TYMHERU Pwrpas tymheru ydi troi dur sydd wedi eu
caledu yn fwy GWYDN. Mae dur caled yn frau ac yn
cracio yn hawdd os yn ei daro iw wneud yn fwy
gwydn rhaid ei gynhesu ai oeri yn aer y gweithle
yn araf -. Maer tabl yn dangos lliwiau tynheru
yn erbyn tymheredd a pwrpas Enghraifft - ar
gyfer creu Driliau bydd angen cynhesu y dur caled
i 240oC neu lliw dark straw a gadael iddo oeri.
TEMPERING Hardened steel is brittle and will
crack if hit the purpose of tempering is to
make it tougher. To temper you heat the steel to
the tempering temperature then cool in air slow
cool. This table shows typical tempering
temperatures with the colour the steel achieves
when heated. Example toughening drills, heat
the steel to 240oC or dark straw and cool in air.
8
ANNEALING Its purpose is to make steel softer
especially metal thats been hardened because of
cold working. Metals harden as you work with them
cold work hardening repeated hitting will
distort the molecules making the metal hard. Even
non ferrous metals suffer copper and aluminium
work harden and need to be annealed or cracks
will appear in the component. You can show work
hardening in the workshop repeatedly bend a
piece of steel or aluminium backwards and
forwards in the vice and eventually it will
snap. Annealing is simple using the annealing
carbon steel chart heat the steel to the
desired temperature depends on carbon , and
allow too cool in the furnace switching off the
furnace for several hours. The metal will be soft
and very weak.
ANELIO Pwrpas anelio ydi meddalhau metel sydd
wedi caledu drwy broses caledu neu trwy weithio.
Mae metalau yn caledu wrth iddynt cael eu
gweithio fel mae metel syn cael ei daro i siap
yn oer maen yn gwaith galedu maer moleciwlau
yn cael ei gywasgu felly yn gwneud y metel yn
galed . Mae defnyddiau anfferus fel copr ac
aliwminiwm yn dioddef o hyn ac angen ei anelio
neu fydd craciau yn dangos yn y cydran. Gallwch
ddangos gwaith-galedu yn y gweithdy plygwch
darn o fetel neu aliwminim nol a blaen yn y feis
ac yn y diwedd gwnaith dorri. Y broses yn syml
rhaid defnyddio y graff ar y dudalen nesaf ich
helpu cynhesu ir tymheredd cywir (dibynnu ar y
carbon) a gadael i oeri yn y ffwrnais araf iawn
iawn gall hyn cymeryd oriau. Fydd y metel wedi
meddalhau ac yn wan. Tymheredd Anelio metalau
Anfferus Non Ferrous Annealing Temperatures
Aliwminiwm / Aluminium 500-550 C
Copr / Copper 650-750 C
Pres / Brass 600-650 C
9
(No Transcript)
10
NORMALEIDDIO Pwrpas normaleiddio ydi newid
adeiladwaith moleciwlau y metel iw gwneud yn
well i dorri ar beiriant. Mae metel caled yn
anodd iw dorri ac arfau , ac mae metel sydd wedi
ei anelio yn anodd iw dorri oherwydd ei fod mor
wan. Defnyddiar normaleiddio i rhyddhau diriant
(stress) mewn cydrannau mawr ar ol iddynt cael ei
gofannu. Proses yn debyg iawn i anelio cynhesu
ir tymheredd cywir maes siart ar y dudalen
nesaf yn dangos y tymheredd tyn erbyn carbon -
ac wedyn ei oeri mewn aer oeri cyflymach.
NORMALISING Its purpose is to change the
molecular structure of the metal to make it
easier for cutting on machines. Hard metals are
difficult to cut with tools, and annealed metal
is very difficult because its so soft and
weak. Normalising is also used to stress relief
large forged components. A very similar process
to annealing heat to temperature shown on
normalising graph (next page) and them cool in
Air much faster cooling.
11