Title: Structural, Magnetic, and Functional Behaviors of Polymerbonded NiCoMnIn Ferromagnetic Shape Memory
1Structural, Magnetic, and Functional Behaviors of
Polymer-bonded Ni-Co-Mn-In Ferromagnetic Shape
Memory Composites
Annual Sigma Xi Student Competition, April 16,
2009
- D. M. Liu1,2, Z. H. Nie2, Y. Ren3, J. Pearson4,
- P. K. Liaw1, Y. D. Wang2
1 Department of Materials Science and
Engineering, The University of Tennessee,
Knoxville, TN 37996, USA 2 Key Laboratory for
Anisotropy and Texture of Materials (Ministry of
Education), Northeastern University, Shenyang
110004, China 3 X-ray Science Division, Argonne
National Laboratory, Argonne, IL 60439, USA 4
Materials Science Division, Argonne National
Laboratory, Argonne, IL 60439, USA
2ACKNOWLEDGES
- This work is supported by the National Science
Foundation Integrative Graduate Education and
Research Training (IGERT) Program, and the
International Materials Institutes (IMI) Program. - This work is supported by the National Natural
Science Foundation of China (Grant Nos. 50725102
and 50531020) and the Ministry of Education of
China with the Specialized Research Fund for the
Doctoral Program of High Education. - Use of the Advanced Photon Source was supported
by the U.S. Department of Energy, Office of
Science, Office of Basic Energy Science, under
Contract No. DE-AC02-06CH11357.
3OUTLINES
- Excellence Disadvantages of Ferromagnetic Shape
Memory Alloys (FSMAs) Ni2MnGa Ni-Co-Mn-In - Motivation of Preparing Ferromagnetic
Ni-Co-Mn-In-Polymer (NCMI-P) Composite - Fabrication and Micrograph of NCMI-P Composite
- Magnetic Properties of NCMI-P Composite
- Synchrotron Studies of NCMI-P Composite with
Temperature, Stress, Magnetic Field - Conclusions
4Critical Scientific Issue
- Excellent Functional Performance
- Disadvantage in Practical Application
Polycrystalline Brittle, low MFIS Single
Crystal High Cost
5MOTIVATION
Composite
N. Scheerbaum, D. Hinz, et.al., Acta Mater. 55,
2707 (2007). J. Feuchtwanger, Ph.D. thesis,
Massachusetts Institute of Technology, Cambridge,
2005.
6Fabrication of Polymer-bonded Ni-Co-Mn-In
Composite with Magnetic Field
Final Volume Ratio11
7Microstructures of NiCoMnIn-Polymer Composite
Optical Microstructure
EBSD Mapping
8Magnetic Properties of NiCoMnIn Composite
?M(5T) 35 emu/g ?M(0.05T)
2.5 emu/g
9In-situ Synchrotron X-ray Study of Martensite
transition During Cooling With/Without Magnetic
Field
0 T
5 T
P(220)
M(127)
Temperature (K)
2? (?)
2? (?)
10In-situ Synchrotron X-ray Study of Martensite
transition During Cooling With/Without Magnetic
Field
Area Ratio
5 T Parent Martensite phase coexist at low
temperature
11In-situ Uniaxial Compression Experiments Using
High-energy X-ray
(040)M
Stress 8 MPa
12Different martensite variants grow in the
different orientation!
13Compression-induced Textured Martensite
360
14Macrostrain ()
Average Volume of Martensite ()
70 MPa
Stress (MPa)
?
Volume of Martensite was evaluated from the
relative integral intensity of martensitic peak
(040)
Remained macrostrain er3.88
?
After unloading
Remained Vm16.3
15In-situ Synchrotron X-ray Study of Reverse
Martensite Transition under a Magnetic Field
Experiment
Line fitting
Vm -2.91063H 24.73432
Volume of Martensite,
Magnetic field, H(T)
M 6.5 T ?Vm 20
16Magnetic-field-induced Strain Recovery Through
Reverse Martensite Transition
Recovery strain 1.75
Volume of Martensite ()
Residual Strain ()
Magnetic field, H (T)
17Conclusion
- Point 1
- The magnetic field blocked the martensite
transformation within Ni45Co5Mn36.6In13.4-polymer
composite, caused the parent and martensite
coexist even at very low temperature. - Point 2
- The Ni45Co5Mn36.6In13.4-polymer composite
showed a stress-induced - martensitic phase-transformation during a
uniaxial compressive - deformation with high ductility.
- Point 3
- A residual strain of 3.88 remained after
unloading. A magnetic-field- - induced strain recovery of ?2 was observed
in this pre-strained - composite. This is attributed to the
magnetic-field-induced reverse - martensitic transformation.
- Point 4
- The large magnetic-field-induced strain,
together with good ductility - and low cost, make the Ni-Co-Mn-In
composites potential candidates for - practical magnetic actuators.